Serat Karbon Lapis Nikel Untuk Industri Tahan Abrasi
Serat karbon berlapis nikel untuk industri tahan abrasi memiliki kekuatan aksial dan modulus yang tinggi, kepadatan rendah, kinerja spesifik tinggi, tidak ada mulur, dan ketahanan yang baik terhadap suhu sangat tinggi dan kelelahan di lingkungan non-oksidasi.
Serat karbon berlapis nikel untuk industri tahan abrasi memiliki koefisien muai panas dan anisotropi yang rendah, ketahanan korosi yang baik, dan transmisi sinar-X yang baik.
Serat karbon berlapis nikel untuk industri tahan abrasi tidak larut dan tidak membengkak dalam pelarut organik, asam, dan basa, dengan ketahanan korosi yang luar biasa.
1. Product Introduction
The nickel plated carbon fiber for abrasion resistant industry can be improved dozens of times after the surface is nickel-plated and metalized, and it is an ideal filler for conductive materials.
The nickel plated carbon fiber for abrasion resistant industry has a uniform nickel-plated layer on the surface and does not peel off after repeated thermal cycles; the nickel layer has excellent electromagnetic shielding performance after being combined with thermoplastic composite materials; it can be used as an additive for powder metallurgy materials to improve strength, plasticity, and thermal stability.
Nickel plated carbon fiber for abrasion resistant industry Applications: powder metallurgy, electromagnetic shielding, conductive plastic film, magnetic film, supercapacitor, and electrode collector.
2. Product Parameter
Item | Test Standard | Unit | Classic Value | |
| Mechanical Properties | Tensile Strength | ISO 11566 | MPa | 3000 |
| Tensile Modulus | ISO 11566 | GPa | 160 | |
| Elongation at break | ISO 11566 | % | 1.3 | |
| Electrical Property | Resistivity | QJ 3074 | Ω cm | 8.23x10-5 |
| Others | Bulk Density | ISO 10119 | g/cm3 | 3.2 |
| Linear Density | ISO 11566 | g/Km | 1630 | |
| Tow | ISO 11566 | ends | 12000 | |
| Filament Diameter | μm | 7.3 | ||
| Coating Thickness | μm | 0.3 | ||
| Nickel Content | % | 50 | ||
| Cross-sectional area | mm2/tow | 0.55 | ||
| Twist | none | |||
3. Product Feature
Good low-frequency shielding performance
Oxidation weight loss temperature up to 750 ℃
Excellent thermal and electrical conductivity
Maintain the original high mechanical properties of nickel plated carbon fiber for abrasion resistant industry
4. Product Application
Supercapacitor
Magnetic thin film
Electromagnetic shielding film
Functional components